| PN-602
is an amino resin based coating. It contains inorganic halogen-free
flame retardant, pigment, plasticizer and other auxiliary
agents. When the coating membrane is exposed to fire, the
flame retardant ingredient decomposes to build up foams on
the surface which act as an insulation layer and fend off
heat and fire.
Characteristics: excellent fireproofing effect,
resistant to acid, alkali, damp heat and weathering, decorative
finish. Suitable for steel, wood structure, electric wire
and cable, etc.
[Properties]
| Flame tolerating time, min |
≥20 |
| Flame propagation ratio |
≤25 |
| Mass loss, g |
≤5 |
| Carbonization volume, cm3 |
≤25 |
| Appearance |
even liquid |
| Particle size, μm |
≤90 |
| Curing time, h |
initial cure ≤5, full cure ≤24 |
| Adhesion |
≤3 |
| Flexibility, mm |
≤3 |
| Impact strength, kg.cm |
≥20 |
| Water resistance, h |
no blister and crack oberserved after 24h. |
| Damp heat resistance, h |
no blister and crack oberserved after 48h. |
[Application method]
1. Surface
preparation is required. All surface must be clean and free
of dust and grease.
2. Stir well
before use. This product can be applied by spray or brush.
Use 200# solvent oil for thinning.
3. Spread
rate is 200g/m2 for eachcoating and 500g/m2 in total. Coating
interval is 8 hours.
4. Unused
product should be kept well closed immediately after use to
prevent solvent loss.
5. Ventilation
is required during operation. Avoid flame.
[Packaging and Storage]
Iron drum, net weight 20kg. Shelt life: one year. This product
is flammable. |